1. Introduction
Fumasep FS-950 membrane is perfluorinated cation exchange membrane - non-reinforced with low resistance, high mechanical stability, low dimensional swelling, and high stability in acidic environment.
2. Delivery
The membrane is the transparent foil, delivered on a backing foil (colorless rigid PET foil). Carefully separate the membrane from the backing foil. The membrane is ready to use.
The standard size of this membrane is 10*10cm & 20*30cm. Customized dimensions can be made upon request.
3. Precautions
Fumatech membranes are highly sensitive to differences in humidity and moisture content. Therefore the membranes can vary +/- 0.5cm from the original cut sizes. Also due to this sensitivity the manufacturer expects wrinkles to form, however soaking the membranes in deionized water will return the membranes to the full size planar state according to the manufacturer.
- Applications: Redox-Flow Battery, e.g. Vanadium-Redox-Flow Battery (VRB), using aqueous acidic conditions.
- Cation Exchange Membrane
- Thickness (dry): 45 - 55 micrometers (μm)
5. Welcome to cite our materials in your papers
Fumasep FS-950, a Perfluorinated cation-exchange membrane (CEM), was obtained from SCI Materials Hub.
6. Handling
Keep membrane package closed / sealed when unused. Unpack membrane only for direct use and process immediately after opening. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane.
Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections.
The membrane is delivered in H-form and dry form. The membrane does not need any pretreatment and is ready for use. Please assemble the membrane in dry form.
If you have any concerns about storage, chemical stability, and pretreatment please feel free to contact us for further information.
Download:
fumasep FS-950 Technical Data Sheet.pdf
| Membrane Properties | |
| Membrane | Cation Exchange Membrane |
| Thickness | 45 - 55 μm (microns) |
| Appearance / Color | Transparent |
| Backing Foil | PET |
| Delivery Form | Dry |
| Reinforcement | None |
| Tensile Strength - max. (MPa) | 36 – 50 MPa |
| Yield Strength at 23°C / 50 % R.H. | 19 – 28 MPa |
| Elongation to Break (%) | 90 – 150 |
| Specific Area Resistance | < 0.1 ohm*cm2 (0.5 M H2SO4) |
| Young’s modulus at 23 °C / 50 % r.h. | 270 – 340 MPa |
| Counter Ion | H+ form |
| Uptake in Vanadyl Sulfate at T =25°C | < 5 wt % |
| Dimensional Swelling in Vanadyl Sulfate at T =25°C | < 4 % |
| Selectivity | > 98 % (0.1 / 0.5 mol/kg KCl at T = 25 °C) |
| Weight Per Unit Area | 8.2 - 9.2 mg*cm-2 |
| Proton Transfer Rate | > 8000 μmol*min-1*cm-2 |
| Bubble Point Test in Water at 25°C | > 3 bar |
| FuMA-Tech cation exchange membrane series in SCI Materials Hub | |||||
| FuMA-Tech CEM Series | Thickness (μm) | pH | Temperature (°C) | Counter ion | Reinforcement |
| CMI-7000S | 450 | 1-10 | 25-90 | Na form | None |
| Fumasep E-620(K) | 20 | 0-14 | 15-40 | K form | None |
| Fumasep E-620-PE(K) | 20 | 0-14 | 15-40 | K form | PE |
| Fumasep F-930-RFD | 30 | -- | -- | H+ | PE |
| Fumasep F-1850 | 50 | -- | -- | -- | None |
| Fumasep F-10120 | 120 | -- | 25-100 | H+ | None |
| Fumasep F-10120-PK | 120 | -- | 25-100 | H+ | PK |
| Fumasep FKB-PK-130 | 130 | 4M KOH | -- | Na/H | PK |
| Fumasep FKD-PK-75 | 75 | -- | -- | H+ | PK |
| Fumasep FKE-50 | 50 | -- | -- | H+ | None |
| Fumasep FKL-PK-130 | 130 | 0-14 | -- | Na form | PK |
| Fumasep FKS-30 | 30 | -- | -- | H+ | None |
| Fumasep FKS-50 | 50 | -- | -- | H+ | None |
| Fumasep FKS-PET-75 | 75 | 0-9 | -- | H+ | None |
| Fumasep FKS-PET-130 | 130 | 0-9 | -- | H+ | None |
| Fumasep FS-830 | 30 | -- | -- | H+ | None |
| Fumasep FS-930 | 30 | -- | -- | H+ | None |
| Fumasep FS-950 | 50 | -- | -- | H+ | None |
| Fumasep FS-990-PK | 90 | -- | -- | H+ | PK |
| Fumapem F-930 | 30 | -- | -- | H+ | None |
| Fumapem F-930-RFS | 30 | -- | -- | H+ | Yes |
| Fumapem F-950 | 50 | -- | -- | H+ | None |
| Fumapem F-14100 | 100 | -- | -- | H+ | None |
| Fumapem FS-930-RFS | 30 | -- | -- | H+ | Yes |
| We Are Committed to Provide the Best Price & Customer Services! | |||||
For internaltional orders, please ask us for quotes via
Email: contact@scimaterials.cn
Tel: +86 153-5789-9751
Wechat: SCI-Materials-Hub
Clik here to put quick orders on our Alibaba shop
Fumasep FS-950 Cation Exchange Membrane | |
Product Code | 15220907 |
| Description | Fumasep FS-950 Cation Exchange Membrane |
| Retail Price (USD$) | $100 (10CM*10CM，Item#：15220907-1010) |
Lead Time & Availability | 1 day & In Stock |
SCI Materials Hub Is Committed to Offering The Best Price & Customer Services! | |
Worldwide shipping via DHL, SF-Express & other requested carriers.
Payments via Bank Transfer, Paypal, Credit card (via Taobao), Alipay, Wechat-pay are accepted.
Partial references citing our materials (from Google Scholar)
Carbon Dioxide Reduction
1. ACS Nano Strain Relaxation in Metal Alloy Catalysts Steers the Product Selectivity of Electrocatalytic CO2 Reduction
The bipolar membrane (Fumasep FBM) in this paper was purchased from SCI Materials Hub, which was used in rechargeable Zn-CO2 battery tests. The authors reported a strain relaxation strategy to determine lattice strains in bimetal MNi alloys (M = Pd, Ag, and Au) and realized an outstanding CO2-to-CO Faradaic efficiency of 96.6% with outstanding activity and durability toward a Zn-CO2 battery.
2. Front. Chem. Boosting Electrochemical Carbon Dioxide Reduction on Atomically Dispersed Nickel Catalyst
In this paper, Vulcan XC-72R was purchased from SCI Materials Hub. Vulcan XC 72R carbon is the most common catalyst support used in the anode and cathode electrodes of Polymer Electrolyte Membrane Fuel Cells (PEMFC), Direct Methanol Fuel Cells (DMFC), Alkaline Fuel Cells (AFC), Microbial Fuel Cells (MFC), Phosphoric Acid Fuel Cells (PAFC), and many more!
3. Adv. Mater. Partially Nitrided Ni Nanoclusters Achieve Energy-Efficient Electrocatalytic CO2 Reduction to CO at Ultralow Overpotential
An AEM membrane (Sustainion X37-50 Grade RT, purchased from SCI Materials Hub) was activated in 1 M KOH for 24 h, washed with ultra-purity water prior to use.
4. Adv. Funct. Mater. Nanoconfined Molecular Catalysts in Integrated Gas Diffusion Electrodes for High-Current-Density CO2 Electroreduction
In this paper (Supporting Information), an anion exchanged membrane (Fumasep FAB-PK-130 obtained from SCI Materials Hub (www.scimaterials.cn)) was used to separate the catholyte and anolyte chambers.
SCI Materials Hub: we also recommend our Fumasep FAB-PK-75 for the use in a flow cell.
5. Appl. Catal. B Efficient utilization of nickel single atoms for CO2 electroreduction by constructing 3D interconnected nitrogen-doped carbon tube network
In this paper, the Nafion 117 membrane was obtained from SCI Materials Hub.
In this paper, Proton exchange membrane (Nafion 117), Nafion D520, and Toray 060 carbon paper were purchased from SCI Materials Hub.
7. National Science Review Confinement of ionomer for electrocatalytic CO2 reduction reaction via efficient mass transfer pathways
An anion exchange membrane (PiperION-A15-HCO3) was obtained from SCI Materials Hub.
8. Catalysis Communications Facilitating CO2 electroreduction to C2H4 through facile regulating {100} & {111} grain boundary of Cu2O
Carbon paper (TGPH060), membrane solution (Nafion D520), and ionic membrane (Nafion N117) were obtained from Wuhu Eryi Material Technology Co., Ltd (a company under SCI Materials Hub).
Batteries
1. J. Mater. Chem. A Blocking polysulfides with a Janus Fe3C/N-CNF@RGO electrode via physiochemical confinement and catalytic conversion for high-performance lithium–sulfur batteries
Graphene oxide (GO) in this paper was obtained from SCI Materials Hub. The authors introduced a Janus Fe3C/N-CNF@RGO electrode consisting of 1D Fe3C decorated N-doped carbon nanofibers (Fe3C/N-CNFs) side and 2D reduced graphene oxide (RGO) side as the free-standing carrier of Li2S6 catholyte to improve the overall electrochemical performance of Li-S batteries.
This paper used more than 10 kinds of materials from SCI Materials Hub and the authors gave detailed properity comparsion.
The commercial IEMs of Fumasep FAB-PK-130 and Nafion N117 were obtained from SCI Materials Hub.
Gas diffusion layers of GDL340 (CeTech) and SGL39BC (Sigracet) and Nafion dispersion (Nafion D520) were obtained from SCI Materials Hub.
Zn foil (100 mm thickness) and Zn powder were obtained from the SCI Materials Hub.
Commercial 20% Pt/C, 40% Pt/C and IrO2 catalysts were also obtained from SCI Materials Hub.
3. Journal of Energy Chemistry Vanadium oxide nanospheres encapsulated in N-doped carbon nanofibers with morphology and defect dual-engineering toward advanced aqueous zinc-ion batteries
In this paper, carbon cloth (W0S1011) was obtained from SCI Materials Hub. The flexible carbon cloth matrix guaranteed the stabilization of the electrode and improved the conductivity of the cathode.
4. Energy Storage Materials Defect-abundant commercializable 3D carbon papers for fabricating composite Li anode with high loading and long life
The 3D carbon paper (TGPH060 raw paper) were purchased from SCI Materials Hub.
5. Nanomaterials A Stable Rechargeable Aqueous Zn–Air Battery Enabled by Heterogeneous MoS2 Cathode Catalysts
Nafion D520 (5 wt%), and carbon paper (GDL340) were received from SCI-Materials-Hub.
Carbon cloth (W0S1011) and other electrochemical consumables required for air cathode were provided by SCI Materials Hub.
Oxygen Reduction Reaction
1. J. Chem. Eng. Superior Efficiency Hydrogen Peroxide Production in Acidic Media through Epoxy Group Adjacent to Co-O/C Active Centers on Carbon Black
In this paper, Vulcan XC 72 carbon black, ion membrane (Nafion N115, 127 μL), Nafion solution (D520, 5 wt%), and carbon paper (AvCarb GDS 2230 and Spectracarb 2050A-1050) were purchased from SCI Materials Hub.
2. Journal of Colloid and Interface Science Gaining insight into the impact of electronic property and interface electrostatic field on ORR kinetics in alloy engineering via theoretical prognostication and experimental validation
The 20 wt% Pt3M (M = Cr, Co, Cu, Pd, Sn, and Ir) were purchased from SCI Materials Hub. This work places emphasis on the kinetics of the ORR concerning Pt3M (M = Cr, Co, Cu, Pd, Sn, and Ir) catalysts, and integrates theoretical prognostication and experimental validation to illuminate the fundamental principles of alloy engineering.
Water Electrolysis
1. International Journal of Hydrogen Energy Gold as an efficient hydrogen isotope separation catalyst in proton exchange membrane water electrolysis
The cathodic catalysts of Pt/C (20 wt%, 2–3 nm) and Au/C (20 wt%, 4–5 nm) were purchased from SCI Materials Hub.
2. Small Science Silver Compositing Boosts Water Electrolysis Activity and Durability of RuO2 in a Proton-Exchange-Membrane Water Electrolyzer
Two fiber felts (0.35 mm thickness, SCI Materials Hub) were used as the porous transport layers at both the cathode and the anode.
3. Advanced Functional Materials Hierarchical Crystalline/Amorphous Heterostructure MoNi/NiMoOx for Electrochemical Hydrogen Evolution with Industry-Level Activity and Stability
Anion-exchange membrane (FAA-3-PK-130) was obtained from SCI Materials Hub website.
Fuel Cells
1. Polymer Sub-two-micron ultrathin proton exchange membrane with reinforced mechanical strength
Gas diffusion electrode (60% Pt/C, Carbon paper) was purchased from SCI Materials Hub.
Characterization
1. Chemical Engineering Journal Electrochemical reconstitution of Prussian blue analogue for coupling furfural electro-oxidation with photo-assisted hydrogen evolution reaction
An Au nanoparticle film was deposited on the total reflecting plane of a single reflection ATR crystal (SCI Materials Hub, Wuhu, China) via sputter coater.
|